Разработка хромистой стали с повышенной коррозионной стойкостью для оболочек твэлов реактора со свинцовым теплоносителем — страница 7

  • Просмотров 529
  • Скачиваний 6
  • Размер файла 466
    Кб

1.Иолтуховский А. Г., Леонтьева- Смирнова М.В. и др. Разработка 12% хромистых сталей нового поколения для атомной техники России., Российская конференция: “ Материалы ядерной техники“, г. Агой, сентябрь 2002 г. 2. Rusanov A.E., Troyanov V.M., Belomytscev Y.S. et. al. Heavy Liquid Metal Coolants in Nuclear Technology, Materials of Conference, Obninsk, 1999, vol.2, p. 633. 3. Bibilashvili Y.K., Ioltukhovskiy A.G., Kazenov Y.I. et al. in: Heavy Liquid Metal Coolants in Nuclear Technology, Materials of Conference, Obninsk, 1999 vol.2, p.337 4. Gorynin I.V. and others. Heavy liquid metal coolants in nuclear technology,

"Structural materials for power plants with heavy liquid metals as coolants", v 1, p. 120, Obninsk, 1999. 5. Gromov B. F., Orlov P.N. and others. Liquid Metal Systems, N.Y., p 339, 1995 6.. Кунин Л.Л. и др. Проблемы дегазации металлов. (Феноменологическая теория). А.Н. СССР, Ордена Ленина институт геохимии и аналитической химии им. В.И. Вернадского, М., " Наука", 1972. 7.Rusanov A.E. and others. Developing and Studying the Cladding Steels for the Fuel Elements of the NPIs with Heavy Coolant, " Heavy liquid metal coolants in nuclear technology", V 2, p. 633, Obninsk, 1999. Higher Corrosion Resistance of Chromium Steel as

Fuel Element Claddings of Lead Cooled Reactor. G.K.Zelenskiy, V.P. Velioukhanov, A.G. Ioltukhovsky, M.V. Leont'eva-Smirnova, V.S. Mitin, I.A. Mescherinova, E.M. Mozhanov, V.P. Pogodin. The Federal State Unitarian Enterprise A.A.Bochvar All-Russia Research Institute of Inorganic Materials VNNNM, p/b 369, Moscow,123060 ABSTRACT As a result of thermodynamic calculations and analysis of different alloying element on corrosion resistance to be tested in lead corrosion-resistant chromium steel experimental compositions Cr13Si2WNbVNAl, Cr14Si2WNbVNAl, Cr16Si2WNbVNAl and Cr18Si2WNbVNAl as well as commercial 12% chromium steels EP 823 and EI 852 were proposed. Static corrosion tests in lead containing 2·10-2 mass % and ≈ 10-4-10-5 mass % oxygen were conducted at 750оC within 500 and

1000 hours. The best results in terms of corrosion resistance under most severe conditions of testing (at 2·10 -2 mass % oxygen in lead) were acquired for affected steels Cr18Si2WNbVNAl and Cr16Si2WNbVNAl. The corrosion-affected zone in these samples was an order of magnitude less than the one in the commercial steel EP 823 considered to be a feasible cladding material for fuel element of BREST-reactor. 4.Тезисы. Разработка хромистой стали с повышенной коррозионной стойкостью для оболочек твэлов реактора со свинцовым теплоносителем. Г.К Зеленский., В.П Велюханов., А.Г. Иолтуховский, В.П. Погодин, В.С. Митин, М.В.

Леонтьева – Смирнова, И.А. Мещеринова, Е.М. Можанов. ФГУП ВНИИНМ им. Академика А.А.Бочвара, 123060 Москва, а/я 369, Россия На основе проведенных термодинамических расчетов и анализа коррозионной стойкости различных легирующих элементов для испыта-ний в свинце выбраны экспериментальные составы коррозионностойких хромистых сталей: Х13С2ВФАР, Х14С2ВБМФАЮ, Х16С2ВБМФАЮ и Х18С2ВБМФАЮ, а также промышленные 12% хромистые стали марок ЭП 823 и ЭИ 852.

Коррозионные испытания образцов в статических усло-виях проводили при температуре 750 оС в течении 500 и 1000 часов в свинце с содержанием кислорода 2 · 10-2 масс.% и ≈ 10-4-10-5 масс.%. В наиболее агрессивных условиях испытаний при содержании кислорода в свинце 2·10 -2 масс. % лучшие результаты по коррозионной стойкости показали стали Х18С2ВБФМАЮ и Х16С2ВБФМАЮ. Величина зоны коррозионного взаимодействия у них была на порядок меньше, чем у